Calcium tungstate Chemical Properties

Melting point:

1620°C

Density 

6.06 g/mL at 25 °C (lit.)

storage temp. 

-20°C

solubility 

Insoluble in H{2}O. Decomposes by hot HCl, HNO{3}

form 

Powder

Specific Gravity

6.062

color 

white

Water Solubility 

insoluble H2O; decomposed by hot HCl, HNO3 [MER06]

Merck 

14,1712

Solubility Product Constant (Ksp)

pKsp: 8.06

Exposure limits

ACGIH: TWA 3 mg/m3
NIOSH: TWA 5 mg/m3; STEL 10 mg/m3

CAS DataBase Reference

7790-75-2(CAS DataBase Reference)

EPA Substance Registry System

Calcium tungsten oxide (CaWO4) (7790-75-2)

Safety Information

WGK Germany 

3

TSCA 

Yes

HS Code 

28418030

MSDS

• Language:English Provider:Calcium tetraoxotungstate
• Language:English Provider:SigmaAldrich
• Language:English Provider:ALFA

Calcium tungstate Usage And Synthesis

Chemical Properties

-325 mesh, 10μm or less 99.9% pure; occurs in nature as mineral scheelite; white tetr powder(s), a=0.524 nm, c=1.138 nm; can be prepared by heating tungstic acid and CaO or CaCO3; used in tumor treatment and in luminous paint [KIR83] [STR93] [MER06]

Large orange octahedral scheelite, Ca(WO4), crystal to 4.5 cm on muscovite, KAl2(AlSi3O10)(OH)2. Pingwu Co., Mianyang pref., Sichuan prov., China.

Uses

Calcium tungsten oxide is used as a luminophore.

Uses

Calcium tungstate can be ued for preparing screens for x-ray observations and photographs; in luminous paints; in scintillation counters.

Application

Calcium tungstate is well known as the phosphor that emits light in λ: 310–700 nm under the excitation light in λ: 220–300 nm. The peak wavelength is positioned at 440 nm, causing it to give off a blue color.

Production Methods

A single crystal is grown from melt by the Czochralski method. Rare earth ions are easy to incorporate into the crystal during growth. Fluorescent films are deposited on a glass substrate through vacuum evaporation using a W filament heated at 2000℃ for about 3 min, followed by thermal annealing in oxygen at 550℃ for 2 h. The film becomes crystalline through this thermal annealing.

General Description

Calcium tungstate (CaWO₄) is an optical material, which can be used as a laser host material for a variety of electronic applications. It has a scheelite structure with luminescence, and thermo-luminescence properties.

Structure and conformation

The space lattice of CaWO4 belongs to the tetragonal system, and its Scheelite structure has lattice constants of a=0.524 nm and c=1.138 nm. The space group is I4_1/a, and there are four formula units per unit cell.

Calcium tungstate(7790-75-2)Related Product Information

• Ammonium paratungstate
• Calcium carbonate
• Calcium carbide
• Calcium Propionate
• SILICOTUNGSTIC ACID HYDRATE
• Calcium chloride
• Calcium gluconate
• Phosphotungstic acid 44-hydrate
• Calcium dobesilate
• Calcium phosphate
• Tungstic acid
• POTASSIUM TUNGSTATE
• LITHIUM TUNGSTATE
• BARIUM TUNGSTATE
• MAGNESIUM TUNGSTATE
• STRONTIUM TUNGSTATE
• AMMONIUM TUNGSTATE 99.99%
• Sodium tungstate