Aluminum diboride Property

Melting point:

decomposes to AlB12 at >920℃ [CIC73]

Density 

3.16

solubility 

soluble in dilute HCl

form 

powder

Water Solubility 

soluble dilute HCl [CIC73]

EPA Substance Registry System

Aluminum boride (AlB2) (12041-50-8)

Safety

WGK Germany 

3

Hazard and Precautionary Statements (GHS)

Aluminum diboride Chemical Properties,Usage,Production

Description

Aluminum diboride (AlB2) is an inorganic compound with a cyclic structure formed by aluminum and boron, and is a high calorific value boron based fuel with high potential for application. Aluminum diboride has a very similar structure to magnesium diboride. It has low specific gravity and high mechanical properties. The longitudinal tensile strength of unidirectionally reinforced boron-aluminum composites is about 1.2~1.7GPa with different processes and raw materials, and the modulus of elasticity is about 200~240GPa. The longitudinal specific modulus of elasticity and specific strength are about 3~5 times and 3~4 times of those of titanium alloy duralumin and alloy steel respectively.

Chemical Properties

powder(s); made by reaction of the elements above 600°C; high neutron absorption; used as a nuclear shielding material [HAW93] [CIC73]

Physical properties

Aluminum diboride：
Crystal system, lattice parameters, structure type, Strukturbericht, Pearson, space group, structure type (Z): Hexagonal a = 300.50 pm; c = 325.30 pm C32, hP3, P6/mmm, AlB type (Z = 1).
Density (ρ/kg.m^–3): 3190; Specific heat capacity (cP/J.kg–1.K–1): 897.87; Vickers or Knoop Hardness (HV or HK/GPa) (/HM): 9.61 HK; Other physicochemical: Temp. transition to AlB at 12 920°C. Soluble in dilute HCl. Nuclear shielding material (uses).

Uses

Aluminum diboride is a solid material that has a high melting point and hardness. It is commonly used to make high-temperature ceramics and materials that are resistant to wear.

Preparation

Aluminum diboride, AlB2, was first synthesized from the elements, amorphous boron and aluminum powder, using an electric arc furnace in a manner similar to that previously described for ReB2. A second sample was prepared in a tube furnace reaction using aluminum metal powder and amorphous boron sealed in a quartz ampule, with a slight excess of boron (nominally AlB2.2). The ampule was placed in the tube furnace, heated to 910 C, and held at this temperature for 12 h before cooling back to ambient temperature. The synthetic preparation of the commercial sample differs from our preparations, involving a reaction between aluminum metal and boron trioxide (B2O3).