ForMaMidiniuM Iodide Property

Melting point:

335°C

Water Solubility 

Soluble in water

form 

powder

color 

White powder/crystals

Safety

Safety Statements 

24/25

HS Code 

29252900

Hazard and Precautionary Statements (GHS)

Symbol(GHS)

Signal word

Warning

Hazard statements

H302Harmful if swallowed

H315Causes skin irritation

H319Causes serious eye irritation

H335May cause respiratory irritation

Precautionary statements

P264Wash hands thoroughly after handling.

P264Wash skin thouroughly after handling.

P270Do not eat, drink or smoke when using this product.

P280Wear protective gloves/protective clothing/eye protection/face protection.

P301+P312IF SWALLOWED: call a POISON CENTER or doctor/physician IF you feel unwell.

P302+P352IF ON SKIN: wash with plenty of soap and water.

P305+P351+P338IF IN EYES: Rinse cautiously with water for several minutes. Remove contact lenses, if present and easy to do. Continuerinsing.

P321Specific treatment (see … on this label).

P330Rinse mouth.

P332+P313IF SKIN irritation occurs: Get medical advice/attention.

P362Take off contaminated clothing and wash before reuse.

P501Dispose of contents/container to..…

ForMaMidiniuM Iodide Chemical Properties,Usage,Production

Applications

Formamidinium lead iodide shows a narrower bandgap than the commonly used methylammonium lead iodide (1.48 eV compared to ~1.57 eV), and hence lies closer to that favourable for optimum solar conversion efficiencies. Spin-coating the formamidinium iodide (FAI) plus PbI2 precursor solution in N,N-dimethylformamide (DMF) initially resulted in discontinuous perovskite films. However, by adding a small amount of hydroiodic acid (HI) to the stoichiometric FAI, extremely uniform and continuous films were formed.
Controlled humidity is another deciding factor that affects the film morphology, crystallinity, and optical and electrical properties of FAPbI3 [2]. 16.6% PCE was achieved with low relative humidity of 2%, with the device efficiency dropped to about half (8.6%) when the humidity was 40%.
Low-volatility additives such as FACl and MACl are good candidates for assisting in the crystallisation of phase pure α-FAPbI3 via the formation of intermediate mixtures, which prohibits the crystallisation of the δ-FAPbI3 phase. It also has been observed that the black perovskite-type polymorph (α-phase), which is stable at relatively high temperatures (above 160 oC), turned into the yellow FAPbI3 polymorph (δ-phase) in an ambient humid atmosphere. Results show that incorporation of MAPbBr3 into FAPbI3 stabilises the perovskite phase of FAPbI3 and improves the power conversion efficiency of the solar cell to more than 18% under a standard illumination of 100 mW/cm2.
With an approach of FAPbI3 crystallisation by the direct intramolecular exchange of dimethylsulfoxide (DMSO) molecules intercalated in PbI2 with formamidinium iodide, device with performance over 20% has been fabricated.

Application

With an approach of FAPbI₃ crystallisation by the direct intramolecular?exchange of dimethylsulfoxide (DMSO) molecules intercalated in PbI₂ with formamidinium?iodide, device with performance over 20% has been fabricated [5].

Description

Formamidinium lead iodide shows a narrower bandgap than the commonly used methylammonium lead?iodide (1.48 eV compared to ~1.57 eV),?and hence lies closer to that favourable for optimum solar conversion efficiencies. With an approach of FAPbI3 crystallisation by the direct intramolecular?exchange of dimethylsulfoxide (DMSO) molecules intercalated in PbI2 with formamidinium?iodide, device with performance over 20% has been fabricated.

Uses

Organohalide based perovskites have emerged as an important class of material for solar cell applications. Our perovskites precursors with extremely low water contents are useful for synthesizing mixed cation or anion perovskites needed for the optimization of the band gap, carrier diffusion length and power conversion efficiency of perovskites based solar cells.

Uses

Formamidinium iodide (FAI) is an organic halide, which can be used as a precursor solution in the fabrication of perovskite-based heterojunction solar cells.