Zinc borate Property

Melting point:

980 °C

Density 

3.64 g/cm3

LogP

-0.292 (est)

CAS DataBase Reference

1332-07-6(CAS DataBase Reference)

EPA Substance Registry System

Zinc borate (1332-07-6)

Safety

Hazardous Substances Data

1332-07-6(Hazardous Substances Data)

Toxicity

Zinc borate 2ZnO3B2O3·3.5H2O has an acute oral toxicity in rats LD50 >10000 mg/kg body weight and acute dermal toxicity in rabbits LD50>10000 mg/kg body weight. It is not a skin irritant and gives a negative response in the Ames mutagenicity test (Kirk-Othmer, 1994).

Hazard and Precautionary Statements (GHS)

Symbol(GHS)

Signal word

Warning

Hazard statements

H319Causes serious eye irritation

H361Suspected of damaging fertility or the unborn child

H400Very toxic to aquatic life

H411Toxic to aquatic life with long lasting effects

Precautionary statements

P201Obtain special instructions before use.

P202Do not handle until all safety precautions have been read and understood.

P264Wash hands thoroughly after handling.

P264Wash skin thouroughly after handling.

P273Avoid release to the environment.

P280Wear protective gloves/protective clothing/eye protection/face protection.

P281Use personal protective equipment as required.

P305+P351+P338IF IN EYES: Rinse cautiously with water for several minutes. Remove contact lenses, if present and easy to do. Continuerinsing.

P308+P313IF exposed or concerned: Get medical advice/attention.

P391Collect spillage. Hazardous to the aquatic environment

P405Store locked up.

P501Dispose of contents/container to..…

Zinc borate Chemical Properties,Usage,Production

Chemical Properties

White, amorphous powder. Soluble in dilute acids; slightly soluble in water. Nonflammable.

Characteristics

Zinc Borate is a Boron based flame retardant compatible with many polymeric matrices. It is effective both in the solid phase and in the gas phase and its strong smoke suppressing action, helps to improve time of rescue in case of fire.
Zinc Borate is a multifunctional flame retardant:
promotes the formation of a protective vitreous layer and of a strong char layer, which reduces the formation of toxic and irritant smoke during the fire
It looses its water of hydration at temperatures above 290°C, cooling the front of the flames and subtracting energy to the fire
It acts as a synergist in conjunction with halogenated compounds, so that lower loadings of halogenated flame retardant additives are needed
It shows a strong synergic effect with antimony trioxide; in presence of alumina trihydrate (ATH) the synergic effect is enhanced
It improves resistance against electrical degradation: high anti-arcing and anti-tracking indexes
It is an afterglow suppressant.

Uses

Zinc borate is prepared as an insoluble double salt from water-soluble zinc and boron compounds. Compounds having varying amounts of zinc, boron, and water of hydration are available. The ratio of these components affects the temperature at which the flame-inhibiting powers are activated, as well as the temperature at which they can be processed. Zinc borates can either be used alone or in combination with other halogen synergists, such as antimony oxide. In some instances zinc borate is also used with alumina trihydrate to form a glass-like substance that inhibits polymer degradation.

Uses

Medicine, fireproofing textiles, fungistat and mildew inhibitor, flux in ceramics.

Application

zinc borate is primarily used as a flame retardant in plastics and cellulose fibers, paper, rubbers and textiles. It is also used in paints, adhesives, and pigments. As a flame retardant, it can replace antimony trioxide as a synergist in both halogen-based and halogen-free systems. It is an anti-dripping and char-promoting agent, and suppresses the afterglow. In electrical insulator plastics it suppresses arcing and tracking.
In halogen-containing systems zinc borate is used together with antimony trioxide and alumina trihydrate. It catalyzes formation of char and creates a protective layer of glass. Zinc catalyzes the release of halogens by forming zinc halides and zinc oxyhalides.
In halogen-free systems, zinc borate can be used together with alumina trihydrate, magnesium hydroxide, red phosphorus, or ammonium polyphosphate. When burning the plastics, a porous borate ceramic is formed that protects the underlying layers. In presence of silica, borosilicate glass can be formed at plastic burning temperatures.
As the partial, or completely EPA approved substitute for containing halogen and other flame retardants, zinc borate is being directly applied to a wide range of plastics and rubber processing such as PVC, PE, PP, and to enhance polyamide, PVC resin, polyphenylene ethylene, epoxy resin, polyester resin, acid ethylene and natural rubber, styrene butadiene rubber, and chloroprene rubber. It can also be applied to the production of paper, fiber fabric, decorative panels, floor leather, wallpaper, carpet, ceramic glaze, fungicides, and paint production to improve flame retardant performance.

Production Methods

Zinc borate (2ZnO·3B2O3·3.5H2O) in general is produced with the reaction between zinc oxide and boric acid. Boric acid is solved in water between temperatures 95ºC and 98ºC and zinc oxide and seed crystal of 2ZnO·3B2O3·3.5H2O is added to this solution at a certain stoichiometric ratio. The reaction continues for a while by mixing and the zinc borate formed is filtered, dried and ground. The boric acid solution is fed to the system as reflux.

Flammability and Explosibility

Not classified

Industrial uses

zinc borate (2ZnO-3B2Ovl5H2O) has a greater flame retardancy than borates used alone.
Zinc compounds perform most of their flame retardant function in the condensed phase. Zinc is used with boron in the form of zinc borate, and with molybdenum in the form of zinc molybdate. Zinc borate can also be used as a flame retardant and smoke suppressant with different polymers. In the case of zinc borate, 2ZnO.3B203.3.5H20, water given off can promote the formation of a cellular char which can act as a good insulator in protecting the underlying polymer or substrate. Moore studied the effects of zinc borate on smoke reduction and flame retardancy of PVC. He reported that smoke generation can be suppressed by over 40% by proper combination of additives without an adverse effect on flame retardancy. The use of zinc borate as a flame retardant and smoke suppressant alone or with other additives, e.g. Sb203, or AI(OH)3, has found wide application in the plastics industry.