Basic information Safety Supplier Related
ChemicalBook >  Product Catalog >  Chemical Reagents >  Silane reagent >  MULLITE

MULLITE

Basic information Safety Supplier Related

MULLITE Basic information

Product Name:
MULLITE
Synonyms:
  • mullite(al6o5(sio4)2)
  • MULLIT
  • MULLITE
  • ALUMINUM OXIDE-SILICON OXIDE
  • ALUMINUM SILICATE, POWDER
  • 92700, MULLITE (LATTICE SPACING, OTHER P
  • MULLITE, LATTICE SPACING AND OTHER PARAMETERS(CRM STANDARD)
  • REFRACTORYMULLITEFIBRE
CAS:
1302-93-8
MF:
Al6O13Si2
MW:
426.05
EINECS:
215-113-2
Product Categories:
  • Inorganics
Mol File:
1302-93-8.mol
More
Less

MULLITE Chemical Properties

Melting point:
1750℃ [JAN85]
Density 
3.16 g/cm3
solubility 
insoluble in H2O, acid solutions, HF
form 
powder
color 
White
Water Solubility 
Insoluble in water.
Exposure limits
ACGIH: TWA 1 mg/m3
OSHA: TWA 15 mg/m3; TWA 5 mg/m3
EPA Substance Registry System
Mullite (Al6O5(SiO4)2) (1302-93-8)
More
Less

Safety Information

Safety Statements 
22-24/25
WGK Germany 
3
RTECS 
BD1450000
TSCA 
Yes

MSDS

More
Less

MULLITE Usage And Synthesis

Description

Mullite [Al6Si2O13 = 3Al2O3·2SiO2], with 71.8 wt.% Al2O,  is an important silicate mineral that occurs in high-silica alumina refractories. Mullite exhibits a high melting point of 1810°C combined with low thermal expansion coefficients (i.e., 4.5 × 10–6 K–1 parallel to the a-axis and 5.7 × 10–6 K–1 parallel to the c-axis), a good mechanical strength with a tensile strength of 62 MPa, and resilience at elevated temperatures that make mullite a highly suitable mineral for highly refractory materials. In nature, mullite is an extremely scarce mineral that occurs only in melted argillaceous inclusions entrapped in lavas from the Cenozoic Era on the Island of Mull, Scotland, but no deposit was found to be economically minable.

Chemical Properties

colorless; rhomb, a=0.7557nm, b=0.76876 nm, c=0.28842 nm; hardness: hot pressed 13.6GPa, sintered 12.7GPa; indentation microfracture 2.02MPa ·m1/2; submicrometer powder(s) can be prepared by hydrolysis of mixed alkoxides, followed by drying and calcining up to 1600°C; sinter, microstructure [SOM91]; phases equilibria in mullite [PAS88]; other data in [HIR89] [ROB67] [MIZ89]

Uses

Mullite is present in the form of needles in porcelain, it is used in high-mullite based products is in hot blast stove checker bricks, melting and firing processes, and is used as a refractory material, manufacture of a type of crucible, steel industry, electronic substrates and protective coatings.

Industrial uses

Artificial mullite, or synthetic mullite, a ceramic material made by a prolonged fusing in the electric furnace of a mixture of silica sand or diasphoric clay and bauxite, has the composition 3Al2O3·2SiO2, has a melting point of 1810 C, and softens at 1650 C.
Mullite occurs in nearly all ceramic products containing alumina and silica but, with the exception of refractories, is seldom introduced as such except as calcined kyanite.
The bricks are resistant to flame and to molten ash, and have a low, uniform coefficient of thermal expansion and a heat conductivity only slightly above that of fireclays. Normally, mullite has very fine crystals that change form and become enlarged after prolonged heating, making the product porous and permeable. For stable high-temperature refractories the mullite is prefused to produce larger crystals. At very high temperatures mullite tends to decompose to form corundum and alkali-silicate minerals of lower heat resistance. Mullite is also used for making spark plugs, chemical crucibles, and extruding dies, and a foamed mullite is used as a uniformly latticed honeycomb structure for lightweight, heat-resistant structural parts.

Synthesis

Synthetic mullite is formed in high-silica alumina refractories during the firing process at high temperature, the major raw materials being kaolin, alumina, and clays and to a lesser extent kyanite, when available. Actually, when a fire clay is fired, its major phyllosilicate mineral, the kaolinite Al4(Si4O10)(OH)8, first gives off its water, and above 800°C an important chemical change takes place with the formation of one of the three aluminosilicate polymorphs (Al2SiO5), i.e., andalusite, kyanite, or sillimanite, and free silica according to the following chemical reaction:
Al4(Si4O10)(OH)8 —> 2Al2SiO5 + 2SiO2 + 4H2O (at T > 800°C)
If firing is carried out above 1595°C, the highly refractory mineral mullite then forms with an additional liberation of free silica that melts according to the following chemical reaction:
3Al2SiO5 —> Al6Si2O13 + SiO2 (at T >1600°C)
For that reason, high-silica alumina refractories containing less than 71.8 wt.% Al2O3 are limited in their use to temperatures below 1595°C. Above 71.8 wt.% Al2O3, mullite alone or mullite plus corundum (α-Al2O3) coexists with a liquidus at 1840°C. Therefore, the use of high-alumina refractories is suited for iron- and steelmaking for firebrick and ladles and furnace linings.

Derivatives

Two grades of synthetic mullite are available for refractories: sintered mullite is obtained by calcination of bauxitic kaolin or a blend of bauxite, aluminas, and kaolin or, to a lesser extent, kyanite; electrofused mullite is made by the electrothermal melting at 2200°C of a mixture of silica sand and bauxite or diasporic clay in an electric-arc furnace. Mullites are formulated to produce dense shapes, some in a glass matrix to yield maximum thermal shock resistance and good mechanical strength. Dense electrofused mullite in a glassy matrix formulated to offer a high-quality economical insulating tubing for thermocouple applications is an extremely versatile and economically viable material. Its workability allows for an extensive range and flexibility in fabrication.
It is well suited for the casting of special shapes. Its typical applications are insulators in oxidizing conditions for noble-metal thermocouples used in conditions up to 1450°C, spark plugs, protection tubes, target and sight tubes, furnace muffles, diffusion liners, combustion tubes, radiant furnace tubes, and kiln rollers. Major producers of sintered mullite are C-E Minerals, Andersonville, GA in the USA, followed by several Chinese producers, while Washington Mills Electro Minerals Corp. in Niagara Falls, NY leads the production of electrofused mullite.

MULLITESupplier

Meryer (Shanghai) Chemical Technology Co., Ltd.
Tel
021-61259108 18621169109
Email
market03@meryer.com
Alfa Aesar
Tel
400-6106006
Email
saleschina@alfa-asia.com
Beijing HwrkChemical Technology Co., Ltd
Tel
010-89508211 18501085097
Email
sales.bj@hwrkchemical.com
Shanghai Hanhong Scientific Co.,Ltd.
Tel
021-54306202 13764082696
Email
info@hanhongsci.com
Shandong Xiya Chemical Co., Ltd
Tel
4009903999 13355009207
Email
3007715519@qq.com