PVB Property

Melting point:

165-185°C

Density 

1.08

refractive index 

1.485

form 

Free-Flowing Powder

color 

White

Water Solubility 

insoluble

Stability:

Stable. Combustible. Dust may form explosive mixture with air. Incompatible with strong oxidizing agents.

CAS DataBase Reference

63148-65-2(CAS DataBase Reference)

EPA Substance Registry System

Polyvinyl butyral (63148-65-2)

Safety

Hazard Codes 

Xi

Risk Statements 

36/37/38

Safety Statements 

26-36-24/25

WGK Germany 

1

RTECS 

TR4955000

HS Code 

39059990

Hazard and Precautionary Statements (GHS)

Symbol(GHS)

Signal word

Warning

Hazard statements

H315Causes skin irritation

H319Causes serious eye irritation

H335May cause respiratory irritation

Precautionary statements

P264Wash hands thoroughly after handling.

P264Wash skin thouroughly after handling.

P280Wear protective gloves/protective clothing/eye protection/face protection.

P302+P352IF ON SKIN: wash with plenty of soap and water.

P305+P351+P338IF IN EYES: Rinse cautiously with water for several minutes. Remove contact lenses, if present and easy to do. Continuerinsing.

P321Specific treatment (see … on this label).

P332+P313IF SKIN irritation occurs: Get medical advice/attention.

P362Take off contaminated clothing and wash before reuse.

PVB Chemical Properties,Usage,Production

Description

Polyvinyl butyral (PVB) is a synthetic resin obtained by the condensation reaction of PVA and butyraldehyde in the presence of acid catalyst. Since the acetalization reaction cannot be carried out completely, the molecular chain of PVB contains three functional groups, butyral, alcohol hydroxyl and acetate, the latter two of which come from PVA. The chemical structure is:
The proportion of these three groups can be controlled by changing the reaction conditions, but they are randomly distributed in the long molecular chain. The proportion and distribution of the three are different, and the properties of PVB are also different.

Chemical Properties

PVB resin is white or slightly yellow amorphous powder, with a particle size of 40–200 μm, fluidity and a density of 1.11 kg.m–1. It is a thermoplastic material, the softening temperature is 60–65°C, the glass transition temperature is 70–78°C, the molding temperature is 120–170°C, and the temperature adaptation range is 10–80°C.
PVB resin is insoluble in water, but soluble in a variety of organic solvents such as alcohols, esters, benzene and ketones. It is miscible with various plasticizer including phthalates, phosphates, and fatty acid ester. It has good compatibility with various resins such as phenolic resin, urea–formaldehyde resin, melamine resin, epoxy resin, nitrocellulose and natural resin. By mixing these resins in an appropriate ratio, the physical and chemical properties are improved, and the cost is reduced.
PVB resin has certain chemical stability, but it can be decomposed in acidic or alkaline (especially acidic) medium. It starts to decompose thermally after being heated to 100°C, and will be almost completely decomposed at 200–240°C. Hydrolysis can occur in dilute acid, at this time intermolecular cross-linking can occur, a small amount of double bonds is formed in the chain, and the acetate group will be further hydrolyzed. Heated in concentrated acid to form a transparent solution, while decomposing into aldehydes. Upon heating in dilute alkali solution with alkali concentration less than 1%, the free acid in PVB resin is neutralized and the thermal stability of the resin is improved. However, when PVB resin is heated with 3% alkaline solution to boiling, the acetate groups can be further hydrolyzed and saponified.

Uses

The main application of poly(vinyl butyral) is as interlayers in safety glass laminates. In this application, a pure (colourless, light-stable) product with high hydroxyl content (for good adhesion) is required. Such material is preferably prepared from poly(vinyl alcohol) rather than directly from poly(vinyl acetate). In a typical process, completely hydrolysed poly(vinyl alcohol) is suspended in ethanol and then butyraldehyde and a small quantity of sulphuric acid (catalyst) are added. The mixture is heated at 800℃ for 6 hours. Water is then added to the product with rapid agitation and the poly(vinyl butyral) is precipitated as granules, which are washed with alkali and dried.
Poly(vinyl butyral) is generally softer than poly(vinyl formal) with lower softening point, hardness and tensile strength. In commercial polymers the hydroxyl content exerts a major influence on the solubility characteristics. Most grades are soluble in alcohols, glycol ethers and dioxan and as the hydroxyl content decreases the polymers become more soluble in ketones and esters.
Poly(vinyl butyral) used in safety glass generally has 78-80% butyral content, 18-19% hydroxyl content and less than 2% acetate content. For this application the polymer is plasticized with an ester such as dibutyl sebacate to the extent of about 30 parts of plasticizer per 100 parts of polymer; the compound is then sheeted by calendering. To produce safety glass, the sheet is placed between two pieces of glass and the laminate is then bonded under heat and pressure.

Application

PVB is mainly used in safety glass interlayer materials. It is also widely used in special coatings, adhesives, ceramic transfer paper, aluminum foil paper and others.
(1) Used as a safety glass interlayer: PVB resin has excellent optical clarity and weather resistance, and can maintain no deformation in a wide range of temperatures. It also has rigidity combined with flexibility and excellent impact resistance. Moreover, it has excellent adhesion efficiency with various glass surfaces. Therefore, the high molecular weight PVB resin is added with 30–40% plasticizer and extruded into a film, which can be used as an interlayer material for safety glass. This is the main purpose of PVB.
(2) Application on ceramic transfer paper: PVB ceramic decal paper is made by pressing a layer of PVC film on wood paper, coating with PVB film and printing patterns for ceramic printing. PVB decal is easy to use, involves low cost and has a high color burn rate.
(3) Application in the coating industry: PVB is used in coatings for preparation of primers, baking paints, varnishes, etc. PVB is widely used in metal coatings. It is mixed with other components such as phenolic, melamine, epoxy and isocyanate to improve the uniformity of the coating film, increase the adhesive strength and elasticity and minimize the coating layer. PVB is used for  textile coating to improve the waterproofness, coloring and adhesion of fabrics.
(4) Application in the adhesive industry: PVB-containing adhesives are mainly high-performance structural adhesives, thermosetting and melt adhesives.
(5) Application on aluminum foil paper: With the rapid development of the national economy and export trade, the requirements for product packaging are getting higher and higher. In order to reduce costs, vacuum aluminized paper with PVB coating has emerged and developed rapidly. At present, this is the largest use of PVB resin in China, accounting for 44% of the total  PVB output.
(6) Other applications: PVB resin can also be applied to prepare special inks such as recording inks, letterpress printing and gravure printing inks. It can also be used to make waterproof fibers, making the fabric antipollution without affecting the appearance, feel and color of the fabric, which is suitable for treatment of almost all fabrics. Furthermore, PVB can be used in dental restorations, wound dressing and wound sutures.