POLY(4-METHYL-1-PENTENE) Property

Melting point:

240 °C

Boiling point:

0.83 °C

Density 

0.835 g/mL at 25 °C

refractive index 

n20/D 1.463

form 

Beads

color 

Clear

CAS DataBase Reference

25068-26-2

EPA Substance Registry System

1-Pentene, 4-methyl-, homopolymer (25068-26-2)

Safety

Safety Statements 

24/25

WGK Germany 

3

HS Code 

39029090

Hazard and Precautionary Statements (GHS)

POLY(4-METHYL-1-PENTENE) Chemical Properties,Usage,Production

Chemical Properties

off-white beads

Chemical Properties

Poly(4-methyl-1-pentene) was first introduced in 1965 by Imperial Chemical Industries Ltd (UK) but since 1975 the polymer has been manufactured solely by Mitsui Petrochemical Industries Ltd. Polymerization is carried out using a Ziegler-Natta catalyst such as titanium trichloride/diethylaluminium chloride in a hydrocarbon diluent at atmospheric pressure and 30-60°C:

The commercial material contains a comonomer, possibly 1-hexene, which enhances clarity. The polymer configuration is predominantly isotactic. Generally, this material has the basic physical properties to be expected from a crystalline polyolefin but in some respects it offers significant improvements over other polyolefins. One outstanding property of poly(4-methyl-l-pentene) is the very low specific gravity, which at 0.83 is the lowest of current polymers. The crystalline melting point is 240°C and the Vicat softening temperature is 179°C; these high values mean that a useful form stability is maintained up to about 200°C. The transparency of the polymer is of a high order, being comparable to poly(methyl methacrylate) and polystyrene. Poly(4-methyl-l-pentene) exhibits resistance to oxidizing and other chemical environments broadly similar to that shown by polypropylene; however, poly(4-methyl-l-pentene) does undergo environmental stress cracking comparable to low density polyethylene. The permeability of poly(4-methyl-I-pentene) to gases and water vapour is considerably higher than that for other polyolefins. Poly(4-methyl-l-pentene) may be extruded and injection moulded using standard equipment. The material has been used in several applications where transparency and heat resistance are required, e.g. medical and laboratory ware.

Uses

Coating for paper food containers for microwave and conventional ovens. Release coatings for food and synthetic leather. Molded into medical labware. Film for decorative laminates and printed circuit boards.